YUFENG WOOL® Ceramic Fiber Vacuum Formed Shapes are made of high quality ceramic fiber bulk, processed by the technique of vacuum forming. Vacuum formed components and customized shapes designed to meet specific application requirements in a wide range of industries.
All Vacuum formed shapes have a lower shrinkage within applicable temperature, and can maintain the characteristics such as insulation, lightweight, etc. During the period of using the products, they won’t be eroded by lots of molten metal.
Key Features
*Excellent thermal shock resistance.
*Low thermal conductivity and heat capacity.
* Long service life and high compression strength.
* Prominent effect of sound-absorption.
*Easy to install and construct.
Applications
*Observation of industrial furnace.Industrial furnace burner, door.
*Plug and launder of Aluminum Products Industry.
*Lining refractory of high-temperature laboratory furnace.
*Thermal insulation of domestic and industrial heating devices
*Non-ferrous metal melting tank padded, casting riser.
*Roller furnace insulation bricks
Item | YUFENG WOOL® STD | YUFENG WOOL® HP | YUFENG WOOL® HZ | YUFENG WOOL® 1600 | |
Classification Temperature (℃) | 1260 | 1350 | 1430 | 1600 | |
Density (kg/m³) | 250-550 | 250-550 | 250-550 | 400-600 | |
Liner Shrinkage (%) at()℃*24h | 1.3 (900) | 1.5 (1100) | 1.6 (1200) | 1.2 (1450) | |
Tensile Strength (Mpa) | 0.7 | 0.7 | 0.7 | 0.6 | |
Thermal Conductivity (w/m.k) | 400(℃) | 0.07 | 0.08 | - | - |
600(℃) | 0.12 | 0.13 | 0.09 | - | |
800(℃) | 0.18 | 0.16 | 0.13 | - | |
1000(℃) | - | - | 0.18 | 0.12 | |
The data are average results of tests under standard procedures and are subject to variation. Results should not be used for specification purposes or creating any contractual obligation. For more information on the safety applications or materials ,please refer to the work practices and material safety data sheet
YUFENG WOOL® Ceramic Fiber Vacuum Formed Shapes are made of high quality ceramic fiber bulk, processed by the technique of vacuum forming. Vacuum formed components and customized shapes designed to meet specific application requirements in a wide range of industries.
All Vacuum formed shapes have a lower shrinkage within applicable temperature, and can maintain the characteristics such as insulation, lightweight, etc. During the period of using the products, they won’t be eroded by lots of molten metal.
Key Features
*Excellent thermal shock resistance.
*Low thermal conductivity and heat capacity.
* Long service life and high compression strength.
* Prominent effect of sound-absorption.
*Easy to install and construct.
Applications
*Observation of industrial furnace.Industrial furnace burner, door.
*Plug and launder of Aluminum Products Industry.
*Lining refractory of high-temperature laboratory furnace.
*Thermal insulation of domestic and industrial heating devices
*Non-ferrous metal melting tank padded, casting riser.
*Roller furnace insulation bricks
Item | YUFENG WOOL® STD | YUFENG WOOL® HP | YUFENG WOOL® HZ | YUFENG WOOL® 1600 | |
Classification Temperature (℃) | 1260 | 1350 | 1430 | 1600 | |
Density (kg/m³) | 250-550 | 250-550 | 250-550 | 400-600 | |
Liner Shrinkage (%) at()℃*24h | 1.3 (900) | 1.5 (1100) | 1.6 (1200) | 1.2 (1450) | |
Tensile Strength (Mpa) | 0.7 | 0.7 | 0.7 | 0.6 | |
Thermal Conductivity (w/m.k) | 400(℃) | 0.07 | 0.08 | - | - |
600(℃) | 0.12 | 0.13 | 0.09 | - | |
800(℃) | 0.18 | 0.16 | 0.13 | - | |
1000(℃) | - | - | 0.18 | 0.12 | |
The data are average results of tests under standard procedures and are subject to variation. Results should not be used for specification purposes or creating any contractual obligation. For more information on the safety applications or materials ,please refer to the work practices and material safety data sheet